Graphene Oxide Film

Graphenea

Graphene Oxide Film

€50.00

Graphene Oxide Film

The Graphene Oxide Film is prepared by the filtration of a Monolayer Graphene Oxide dispersion.

Properties

  • · Diameter: 4cm
  • · Thickness: 12-15 μm
  • · Non-conductive

Millipore filter specifications

  • · Pore Size: 0.025 μm
  • · Thickness: 105 μm
  • · Porosity: 70%
  • · Material: Biologically inert mixtures of cellulose acetate and cellulose nitrate

Elemental Analysis

  • · Carbon: 49 – 56%
  • · Hydrogen: 0 – 1%
  • · Nitrogen: 0 – 1%
  • · Sulfur: 0 – 2%
  • · Oxygen: 41 – 50%

Quality control

Our Graphene Oxide Filters are subjected to a rigorous QC in order to ensure a high quality and reproducibility.

  • ·Elemental Analysis
  • If your application requires more specific quality control, please do not hesitate to contact us.

    Applications

    • · Biomedical, membranes, Graphene research...

    Publications

    “Precise and Ultrafast Molecular Sieving Through Graphene Oxide Membranes”, Science 343, 752 (2014)

    “Large-area ultrathin films of reduced graphene oxide as a transparent and flexible electronic material ”, Nature Vol. 3, May 2008

    Downloads

    €50.00

    Frequently Asked Questions

    A: The GO is a polydisperse material where most of the particles have a size around 15 μm, as shows the next results measured by laser diffraction:

    • - D90 29.05 - 32.9 μm
    • - D50 14.30 - 16.6 μm
    • - D10 5.90 - 6.63 μm

    A: GO is extensively washed and some metal traces can be found in ppb.

    A: Our GO is dispersed in water because it is very stable and no surfactant is needed. GO is functionalized with epoxy, alcohol and COOH groups on its edges. These functional groups make GO highly hydrophilic and also it loses part of its sp2 hybridization, making GO insulating. In order to recover conductivity is has to be reduced. We can work with other solvents, please contact us to know more about it.